Loctite IND 406 Black – High Temperature Industrial 3D Printing Resin

Home » 3D Printer Shop » 3D Printing Resin » Loctite Industrial 3D Printing Resin » Loctite IND 406 Black – High Temperature Industrial 3D Printing Resin
Loctite IND 406 High temp industrial 3d resin
loctite IND 406 high temp resin specs
IND 406 accelerated age UV test

Loctite IND 406 Black – High Temperature Industrial 3D Printing Resin

$299.00 +gst

In stock

LOCTITE 3D IND406 is the toughest High Temperature 3D Printing Resin available.

A common problem with most high temperature resins is that they are quite brittle.
But the IND 406 BK is a high-strength, high elongation engineering plastic with good impact and high temperature resistance up to 107 C.

It has also been weather tested with UV to perform well outdoors with minimal change to mechanical properties.

Stiffness, toughness and thermal durability make this the ideal material for a wide variety of tools in the production floor.
Thanks to excellent chemical resistance & immersion testing, IND 406 is perfect for final parts production in Automotive manufacturing.
The product is ideal for fixtures, interior and machinery parts.

LOCTITE 3D IND406 can be printed in various resin 3d printers and parts can be machined, tapped, or polished for final finish.

In stock

SKU: 33125 Categories: , , , , , ,

Description

LOCTITE IND406 is a tough, rigid and durable 3D printing resin that performs well in industrial applications requiring good mechanical properties even at high temperatures up to 120C.
IND406 is a great alternative for traditional injection molded plastics such as ABS and PP.
It offers good all-round strength, impact resistance, and high elongation allowing it to be used in snap fit applications.

Key Benefits:

  • HDT at 0.455MPA = 107 °C
  • Tensile Stress at Break – 55 MPa
  • Young’s Modulus – 1600 MPa
  • Elongation at Break – 25%
  • Shore Hardness – 79D

Biocompatibility: ISO 10993 -5/-23 passed

Color: Black

Technical Specifications:

Property Measure Value Method
Young’s Modulus MPa 1610 ± 40 ASTM D638
Tensile Stress at Break MPa 55 ± 1 ASTM D638
Elongation at Break % 25 ± 4 ASTM D638
Flexural Modulus MPa 1880 ± 25 ASTM D790
Flexural Stress at Break MPa – ASTM D790
Flexural Strain at Break % > 5 ASTM D790
IZOD Impact (Notched) J/m 35 ± 8 ASTM D256
Shore Hardness (3s) D 79 ± 1 ASTM D2240
HDT at 0.455 MPa °C 107 ± ASTM D648
HDT at 1.82 MPa °C 81 ± 2 ASTM D648
Water Absorption (24 h) % 1.4 ASTM D570
Water Absorption (72 h) % 2.6 ASTM D570
Solid Density g/cm³ 1.19 ASTM D792
Thermal Conductivity mW/m·K 206 ± 3 ASTM D5930
Heat Capacity J/(g·K) 1.46 ± 0.04 ASTM D5930
Horizontal flame spread speed (1.4 mm thickness) mm/min 28 (Pass) DIN 75200
Cytotoxicity – Comply ISO10993-5
Irritation – Comply ISO10993-23*

 

This resin has exceptional chemical resistance as well as heat aging properties.

For the full TDS, please see here https://dm.henkel-dam.com/is/content/henkel/Loctite-3D-IND406