Luvocom 3F PAHT 9825 Nylon 2.85mm 3D Filament

Luvocom 3F PAHT 9825 Nylon 2.85mm 3D Filament

$50.00 +gst

Out of stock

Nylon PA6 3D Filament Made in Netherlands by 3D4Makers – 750g 2.85mm

Luvocom® 3F PAHT 9825 NT Filament is a Low Moisture High-temperature polyamide that doesn’t have Carbon Fiber in it.

High Strength, High Flexibility, High Surface Abrasion Resistance, Excellent Chemical & Petroleum Resistance.
Nylon is suited perfectly in lubricating applications for bearings, gears & pulleys with belts.

This roll of Nylon PA6 in 2.85mm designed to work with most 3mm compatible 3d printers like Creatbot, Ultimaker, Taz etc

Its water uptake takes about 4 times longer to reach saturation point compared to other PA6 on the market.
And its saturation point is 5 times lower than conventional PA6 materials, meaning it has very little mositure rentention. 

This particular engineering polymer grade is tailored made for the 3D printing industry to match the injection molding strength requirements and focusing on the serial production of end-parts.

The filament can be used on conventional FFF / FDM 3D printing systems due to the enhanced printability, & improved layer bonding even without the use of a heated chamber.

Out of stock

Description

Material properties

Description Value Test method
Density 1,20 g/cm3 ISO 1183-3
Tensile  strength (at 23°C/50% rh) 85 MPa ISO 527
Elongation (at 23°C/50% rh)
3,6 %
ISO 527
Modulus of Elasticity  (at 23°C/50% rh) 3,4 GPa ISO 527
Heat Distortion Temp. 90 °C ISO 75
Continuous Service Temp. 120 °C UL 746B
Maximum (short term) Use Temp. 160  °C /
Thermal Conductivity 0,3 W/mK HOT-DISK

Printer recommendations 

Description Value
Printer nozzle temperature 260 – 285°C
Heated bed temperature 60 – 80°C
Print Speed 40 – 60 mm/s
Bed Adhesion Magigoo PA on glass or a PEI Sheet
Pre drying recommendations 100°C, 4 – 6 hours or 80°C, 12 hours

*Printing profile available in Ultimaker Marketplace (Ultimaker certified material)